Keywords : Attapulgite
Engineering and Technology Journal,
2014, Volume 32, Issue 10, Pages 2364-2375
Tremendous research efforts have been directed to investigate the possibility of using the Iraqi Attapulgite clay as a mineral admixture to improve some properties of concrete. To investigate about this clay as a pozzolan, many experimental work need to be done to find the suitable conditions of temperature and time of calcinations. To study the influence of calcinations temperature, different samples of Attapulgite were prepared.
The samples were grinded to fineness 2109 m2/ kg , then burned to ( 550 , 600 , 650 , 700 , 750 , 775 and 800)˚C at 1/2 hour , respectively . According to the American Standard Specifications, the strength activity index was conducted on the cubic specimens with dimensions (50 * 50 * 50) mm. The results showed that the optimum calcinations temperature was 750 ˚C. The Attapulgite samples were prepared at ( 1/2 , 1 , 1 1/2 , 2 ) hours , respectively and the temperature was 750 ˚C , then strength activity index was conducted . The results showed that the optimum calcinations time was 1/2 hour.