Keywords : Electrospun


Multiwall Carbon Nanotube / Polyvinyl Alcohol Nanofibers Film, Electrical Conductivity Improvement

Akram R. Jabur

Engineering and Technology Journal, 2020, Volume 38, Issue 3A, Pages 431-439
DOI: 10.30684/etj.v38i3A.530

Conductive polymer films were prepared of polyvinyl alcohol (PVA) with (0, 2, 4, 6, 8, and 10) wt. % multiwalled carbon nanotubes (MWCNTs) by electrospinning technique. The morphologies of the synthesized films were tested by scanning electron microscopy (SEM). Average fiber diameters gauged statically was (115nm) for (PVA/10 wt. % MWCNT film) while (170nm) for pure PVA electro spun film. Electrical conductivity (EC) of Polymeric nanofiber films improve by increasing MWCNT addition concentration from (3.69 × 10-7 S/ cm) for the pure (PVA) film to (1.24 ×10-2 S/cm) for the film with 10 wt. % MWCNT. The maximum stress of PVA film were increased by adding MWCNTs concentration, the modulus of elasticity was enhanced from 12.87 MPa for pure PVA to 49.89 MPa for PVA/8wt% MWCNT.