Studying the Erosion Corrosion Behavior of NiCrAlY Coating Layer Applied on AISI 446 Stainless Steel Using Thermal Spray Technique

Ghufran J. Matrood; Ahmed M. Al-Gaban; Hussain M. Yousif

Engineering and Technology Journal, 2020, Volume 38, Issue 11, Pages 1676-1683
DOI: 10.30684/etj.v38i11A.1691

Erosion-Corrosion behavior of NiCrAlY coatings deposited on 446 stainless steel samples by flame thermal spraying was performed in this research. The hardness of uncoated and coated sample is measured, using HVS-1000 Digital Micro hardness Tester. The results of hardness show that the coated samples have higher hardness than uncoated samples. Microstructure and phase analysis of the coating layer was observed by using optical microscope, X-ray diffraction (XRD), and SEM respectively. Erosion –Corrosion test was performed in different period of time (6, 12, and 18 hr.) using the erosion-corrosion system. The result shows that because of uniform distribution and homogeneous of coating layer, weight loss was very low and approximately equal in all period of testing time.