Synthesis of Nano-TiO2 Thin Films by Sol-gel Dip-coating Method

Bushra R. Mahdi; Abass F. Al.mamori; Adnan meship Mahdi

Engineering and Technology Journal, 2015, Volume 33, Issue 7, Pages 1303-1312

Synthesis of titanium dioxide (TiO2) Thin film on three microscope glasses using sol-gel method has been studied intensively. The starting materials were titanium(III)chloride, Ammonium Hydroxide. The components were mixed together to form the sol. Then, at 50℃ heating and ageing was applied to form stable sol-gel . Every glass substrate dipping in sol-gel beaker for period time (1,3,5)min respectively, for obtaining different thickness films. To evaluate the performance of films, After annealing at 500℃ , the crystallinity of the films was determined by using the x-ray diffractometer (XRD). The change on the surface morphology was observed using Atomic Force Microscope(AFM). Finally, Optical properties measurements Absorbance (A) and transmittance(T)) for (TiO2) films were studied by UV-Visible spectrometer.
analysis on the films. It has been successfully shown that the anatase crystalline phase was observed when the TiO2 thin film was annealing at 500°C. The roughness and the crystalline size of TiO2 thin film changed with the thickness. The minimum grain size( 6.92) nm for thickness 1.2µm UV-visible studying that absorption is maximum at UV spectrum (opaque) and the transmittance is maximum at the visible spectrum