The Effect of Ceramic Particale Oxides addition on Wear Resistance of Composite Material for Aluminum Base Alloy
Engineering and Technology Journal,
2012, Volume 30, Issue 7, Pages 1249-1264
AbstractTo The aim of this research is to study the effect of 5 wt % Al2O3
addition Al- base alloy on sliding wear resistance under dry sliding
conditions using pin- on- disc machine . Wear test was conducted
after squeeze casting under different pressure ( 30 , 60 , 90) Mpa.
The results show that wear rate for Al- base alloy composites
increases with increasing applied load but decreases with increasing
sliding speed conditions . The composites which casting at 90 Mpa
pressure represents lower wear rate than those which cast at 30, 60 Mpa
pressure and the base alloy . The results also observed that the
coefficient of friction increasing with increasing sliding time but reaches to the steady state after 200 sec. The microhardness and ultimate tensile strength increases with increasing squeeze casting pressure.